https://repositorio.ufba.br/handle/ri/37995| Tipo: | Dissertação |
| Título: | Painéis sanduíche com núcleo de concreto leve contendo endocarpo de dendê e faces cimentícias reforçadas com fibras curtas de sisal |
| Título(s) alternativo(s): | Sandwich panels with lightweight concrete core containing palm endocarp and cementous faces reinforced with short sisal fibers |
| Autor(es): | Nunes, Mariana Santos |
| Primeiro Orientador: | Lima, Paulo Roberto Lopes |
| metadata.dc.contributor.advisor-co1: | Carvalho, Ricardo Fernandes |
| metadata.dc.contributor.referee1: | Lima, Paulo Roberto Lopes |
| metadata.dc.contributor.referee2: | Carvalho, Ricardo Fernandes |
| metadata.dc.contributor.referee3: | Silva, Francisco Gabriel Santos |
| metadata.dc.contributor.referee4: | Gloria , M’Hamed Yassin Rajiv da |
| Resumo: | O uso de painéis sanduíche se apresenta como boa alternativa na construção civil, pois, além de possuir baixo peso próprio e elevada resistência, podem ser pré-fabricados, facilitando o transporte e montagem na obra. O objetivo geral desta pesquisa foi desenvolver um painel sanduíche com núcleo de concreto leve contendo resíduo agroindustrial e faces em material cimentício composto com fibras vegetais. Na composição do concreto leve foi utilizado endocarpo do dendê em substituição do agregado graúdo convencional. Os endocarpos passaram por uma limpeza prévia e foram triturados antes de serem inseridos na matriz. Quatro diferentes composições foram testadas para o concreto visando encontrar uma proporção de endocarpo e de água que promovesse um concreto com baixa densidade e resistência satisfatória. O endocarpo foi testado nas misturas nas proporções de 50%, 100% e 150% em relação a massa de aglomerante e o teor a/aglo em 0,35 e 0,45. As faces do painel foram fabricadas com argamassa reforçada com fibras curtas de sisal. Estas fibras foram hornificadas antes de serem inseridas na matriz, buscando evitar a variação dimensional e por consequência a perda de aderência na interface fibra-matriz. Todos os traços testados para o concreto resultaram em um material com baixa densidade, em que a massa específica ficou abaixo de 1504 kg/m³. O maior valor de resistência à compressão obtida para o concreto foi de 18,05 MPa. Os resultados encontrados para os painéis seguiram o mesmo comportamento do núcleo para a maior parte das propriedades testadas. A massa específica dos painéis não ultrapassou 1480 kg/m³. Em relação ao comportamento mecânico, para a compressão axial longitudinal, obteve-se o valor de 12,81 MPa. O concreto e o painel que apresentaram melhores resultados foram os confeccionados com 100% de teor de endocarpo e 0,35 de fator a/aglo. Desta forma, conclui-se que é possível confeccionar concretos com baixo peso específico utilizando o endocarpo do dendê, promovendo uma nova utilização e o aumento do valor agregado desse resíduo. |
| Abstract: | The use of sandwich panels is presented as a good alternative in civil construction, because, in addition to having low weight and high strength, they can be prefabricated, facilitating transport and assembly on site. The general objective of this research was to develop a sandwich panel with a light concrete core containing agro-industrial residue and faces in cement material composed with vegetable fibers. In the composition of light concrete, palm endocarp was used to replace conventional coarse aggregate. The endocarps were previously cleaned and crushed before being inserted into the matrix. Four different compositions were tested for the concrete in order to find a proportion of endocarp and water that would promote a concrete with low density and satisfactory strength. The endocarp was tested in the mixtures in the proportions of 50%, 100% and 150% in relation to the binder mass and the w/aglo content at 0.35 and 0.45. The panel faces were manufactured with mortar reinforced with short sisal fibers. These fibers were hornified before being inserted into the matrix, seeking to avoid dimensional variation and, consequently, the loss of adhesion at the fiber-matrix interface. All the tested mixes for the concrete resulted in a material with low density, in which the specific mass was below 1504 kg/m³. The highest value of compressive strength obtained for the concrete was 18.05 MPa. The results found for the panels followed the same behavior as the core for most of the tested properties. The specific mass of the panels did not exceed 1480 kg/m³. Regarding the mechanical behavior, for the longitudinal axial compression, the value of 12.81 MPa was obtained. The concrete and the panel that presented the best results were those made with 100% endocarp content and 0.35 w/aglo factor. In this way, it is concluded that it is possible to make concrete with low specific weight using the endocarp of palm oil, promoting a new use and increasing the added value of this residue. |
| Palavras-chave: | Comportamento mecânico Endocarpo do dendê Painel sanduíche Sisal |
| CNPq: | CNPQ::ENGENHARIAS |
| Idioma: | por |
| País: | Brasil |
| Editora / Evento / Instituição: | Universidade Federal da Bahia |
| Sigla da Instituição: | UFBA |
| metadata.dc.publisher.department: | Escola Politécnica |
| metadata.dc.publisher.program: | Programa de Pós-graduação em Engenharia Civil (PPEC) |
| Tipo de Acesso: | CC0 1.0 Universal |
| metadata.dc.rights.uri: | http://creativecommons.org/publicdomain/zero/1.0/ |
| URI: | https://repositorio.ufba.br/handle/ri/37995 |
| Data do documento: | 30-Set-2021 |
| Aparece nas coleções: | Dissertação (PPEC) |