Título: Effect of thermal aging conditions on the corrosion properties and hardness of a duplex stainless steel
Título(s) alternativo(s): Materials Research
Autor(es): May, José Eduardo
Souza, Carlos Alberto Caldas de
Nascente, Pedro Augusto de Paula
Soares, Paulo
Lepienski, Carlos Mauricio
Kuri, Sebastião Elias
Autor(es): May, José Eduardo
Souza, Carlos Alberto Caldas de
Nascente, Pedro Augusto de Paula
Soares, Paulo
Lepienski, Carlos Mauricio
Kuri, Sebastião Elias
Abstract: The corrosion properties of a 22.5 wt. (%) Cr duplex stainless steel were investigated after long-term aging of 3000, 5000 and 7000 hours at 300 and 400 ºC. The corrosion resistance was measured based on mass loss in a FeCl3 10 wt. (%) solution and electrochemical measurements in a 0.1 M H2SO4 solution. The results indicate that the corrosion resistance decreased steadily up to 5000 hours of aging. However, the samples subjected to 7000 hours of aging showed better corrosion resistance than those aged for 3000 and 5000 hours. This effect is attributed to the phase transformation that occurs during aging, a finding which was confirmed by hardness, transmission electron microscopy and X-ray photoelectron spectroscopy measurements.
Palavras-chave: Duplex stainless steel
Corrosion
Structural characterization
Long-term aging
URI: http://www.repositorio.ufba.br/ri/handle/ri/4904
Data do documento: 2010
Aparece nas coleções:Artigo Publicado em Periódico (PEI)

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
v13n4a03.pdf709,03 kBAdobe PDFVisualizar/Abrir
Mostrar registro completo do item Visualizar estatísticas


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.