dc.description.abstractIn this work a series of Ni/La2O3 catalysts were synthesized in order to assess the influence of synthesis method as well as the influence of barium on the catalytic properties. Initially, the catalytic precursors La1-xBaxNiO3 (x = 0.0; 0.05; 0.1 and 0.2) and NiO/La2O3 were prepared by the citrate and wet impregnation methods, respectively. The precursors were characterized by the techniques TGA, XRD, XRD-H2, XRD-CH4/CO2 and TPR-H2. Moreover, catalytic evaluation was realized followed by TPO analysis to evaluate carbon deposition. The XRD analysis indicated that the synthesis methods were able in obtain the desirable phases. Nonetheless, the barium presence led to BaCO3 segregation. The in situ diffraction results under reducing atmosphere indicated that the perovskite reduction mechanism occurs in two main steps. Furthermore, after reduction process, BaCO3 is a present phase in barium-based catalysts. Under reaction atmosphere, the diffraction results indicated that the catalysts are susceptible to oxidation Ni/NiO, however the barium presence makes it more resistant. The TPR results showed that barium insertion does not change the reduction process, nonetheless the higher reduction temperature for these precursors suggest a more intense metal-support interaction. The TPSR analysis and catalytic evaluation pointed out that the catalysts were active and selective to synthesis gas, being that the catalysts coming from the perovskite structure showed a better performance when compared to the catalyst synthesized by wet impregnation. The BaCO3 presence on the barium-content catalysts, although led to decreased activity of the catalysts, it suggested a higher carbon species oxidizing capacity. Such proposal was confirmed by TPO analysis, being the catalysts that presented similar performance, La0.9Ba0.1NiO3 and La0.8Ba0.2NiO3, the last one showed the highest resistance to carbon deposition.pt_BR
dc.description.sponsorshipCNPqpt_BR
dc.languageporpt_BR
dc.publisherUniversidade Federal da Bahiapt_BR
dc.rightsAcesso Abertopt_BR
dc.subjectReforma seca do metanopt_BR
dc.subjectCatalisadores de níquelpt_BR
dc.subjectCarbonato de báriopt_BR
dc.subjectDry reforming of methanept_BR
dc.subjectNickel catalystspt_BR
dc.subjectBarium carbonatept_BR
dc.titleEstudo de catalisadores a base de níquel na reação de reforma seca do metano e a influência do bário nas propriedade catalíticaspt_BR
dc.title.alternativeStudy of nickel-based catalysts in the reaction of methane dry reform and the influence of the bead on catalytic propertypt_BR
dc.typeDissertaçãopt_BR
dc.publisher.programPrograma de Pós-Graduação em Química pt_BR
dc.publisher.initialsUFBApt_BR
dc.publisher.countryBrasilpt_BR
dc.subject.cnpqCNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::FISICO-QUIMICApt_BR
dc.contributor.advisor1Brandão, Soraia Teixeira-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/1618632130640544pt_BR
dc.contributor.referee1Brandão, Soraia Teixeira-
dc.contributor.referee1Latteshttp://lattes.cnpq.br/5905411845829250pt_BR
dc.contributor.referee2Rodrigues, Lilian Maria Tosta Simplício-
dc.contributor.referee2Latteshttp://lattes.cnpq.br/9124932218814921pt_BR
dc.contributor.referee3Frety, Roger Thomas François-
dc.contributor.referee3ID0000-0002-4532-2105pt_BR
dc.contributor.referee3Latteshttp://lattes.cnpq.br/7983227852851755pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/1618632130640544pt_BR
dc.description.resumoNeste trabalho uma série de catalisadores Ni/La2O3 foram sintetizados com a finalidade de avaliar a influência do método de síntese bem como a influência do bário nas propriedades catalíticas. Inicialmente, os precursores catalíticos La1-xBaxNiO3 (x = 0,0; 0,05; 0,1 e 0,2) e NiO/La2O3 foram preparados pelos métodos citrato e impregnação por via úmida, respectivamente. Os precursores foram caracterizados através das técnicas TG, DRX, DRX-H2, DRX-CH4/CO2 e TPR-H2. Além disso, foram feitas avaliações catalíticas seguidas de ensaios de TPO para avaliar a deposição de carbono. As análises de DRX indicaram que os métodos de síntese utilizados foram eficientes na obtenção das fases desejadas. No entanto, a presença de bário levou à segregação de BaCO3. Os resultados de difração in situ sob atmosfera redutora indicaram que o mecanismo de redução dos precursores perovskitas ocorre em duas etapas principais. Além disso, após processo de redução, BaCO3 é uma fase presente nos catalisadores constituídos por bário. Sob atmosfera reacional, os resultados de difração indicaram que os catalisadores são sujeitos à oxidação Ni/NiO, porém a presença de bário torna os catalisadores mais resistentes à oxidação. Os resultados de TPR indicaram que a inserção de bário não altera o processo de redução, no entanto a maior temperatura de redução para esses precursores sugere uma interação metal-suporte mais intensa. As análises de TPSR e a avaliação catalítica apontaram que os catalisadores são ativos e seletivos a gás de síntese, sendo que os catalisadores provenientes da estrutura perovskita apresentaram melhor desempenho quando comparados ao catalisador obtido por via úmida. A presença de BaCO3 nos catalisadores constituídos por bário, embora tenha promovido a diminuição da atividade do catalisador, sugeriu uma maior capacidade oxidante das espécies de carbono. Tal proposta foi confirmada através dos ensaios de TPO, sendo os catalisadores que apresentaram desempenho semelhante, La0,9Ba0,1NiO3 e La0,8Ba0,2NiO3, o de maior teor de bário apresentou maior resistência à deposição de carbono.pt_BR
dc.publisher.departmentInstituto de Químicapt_BR
Aparece nas coleções:Dissertação (PPGQUIM)

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Dissertação_Ruan Gomes.pdf2,6 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.