Título: Development of Fe–Ni/YSZ–GDC electrocatalysts for application as SOFC anodes: XRD and TPR characterization and evaluation in the ethanol steam reforming reaction
Título(s) alternativo(s): International Journal of Hydrogen Energy
Autor(es): Fiuza, Raigenis da Paz
Silva, Marcos Aurélio da
Boaventura Filho, Jaime Soares
Autor(es): Fiuza, Raigenis da Paz
Silva, Marcos Aurélio da
Boaventura Filho, Jaime Soares
Abstract: Electrocatalysts based on Fe–Ni alloys were prepared by means of modified Pechini and physical mixture methods and using on a composite of Yttria Stabilized Zirconia (YSZ) and Gadolinia-Doped Ceria (GDC) as support. The former method was based on the formation a polymeric precursor that was subsequently calcined; the later method was based on the mixture of NiO and the support. The resulting composites had 35 wt.% metal load and 65 wt.% support (70 wt.% YSZ and 30 wt.% GDC mixture) (cermets). The samples were then characterized by Temperature-Programmed Reduction (TPR) and X-Ray Diffraction (XRD) and evaluated in the ethanol steam reforming at 650 °C for 6 h in the temperature range of 300–900 °C. The XRD results showed that the bimetallic sample calcined at 800 °C formed a mixed oxide (NiFe2O4) with a spinel structure, which, after reduction in hydrogen, formed Ni–Fe alloys. The presence of Ni was observed to decrease the final reduction temperature of the NiFe2O4 species. The addition of iron to the nickel anchored to YSZ–GDC increased the hydrogen production and inhibited carbon deposition. The resulting bimetallic 30Fe5Ni sample reached an ethanol conversion of about 95% and a hydrogen yield up to 48% at 750 °C. In general, ethanol conversion and hydrogen production were independent of the metal content in the electrocatalyst. However, the substitution of nickel for iron significantly reduced carbon deposition on the electrocatalyst: 74, 31, and 9 wt.% in the 35Ni, 20Fe15Ni, and 30Fe5Ni samples, respectively.
Palavras-chave: Anode
Carbon deposition
Ethanol
Solid oxide fuel cell (SOFC)
Iron–nickel catalyst
Reforming
URI: http://www.repositorio.ufba.br/ri/handle/ri/12400
Data do documento: 2010
Aparece nas coleções:Artigo Publicado em Periódico (Química)

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
1-s2.0-S0360319910013455-main.pdf
  Restricted Access
941,93 kBAdobe PDFVisualizar/Abrir Solicitar uma cópia
Mostrar registro completo do item Visualizar estatísticas


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.