https://repositorio.ufba.br/handle/ri/5493
Tipo: | Artigo de Periódico |
Título: | Durability of Resin Cement Bond to Aluminium Oxide and Zirconia Ceramics after Air Abrasion and Laser Treatment |
Título(s) alternativo(s): | Journal of Prosthodontics |
Autor(es): | Foxton, Richard M. Cavalcanti, Andrea Araújo de Nóbrega Nakajima, Masatoshi Pilecki, Peter Sherriff, Martyn Melo, Luciana Watson, Timothy F. |
Autor(es): | Foxton, Richard M. Cavalcanti, Andrea Araújo de Nóbrega Nakajima, Masatoshi Pilecki, Peter Sherriff, Martyn Melo, Luciana Watson, Timothy F. |
Abstract: | Purpose: The erbium laser has been introduced for cutting enamel and dentin and may have an application in the surface modification of high-strength aluminum oxide and zirconia ceramics. The aim of this study was to evaluate the durability of the bond of conventional dual-cured resin cements to Procera Al2O3 and zirconium oxide ceramics after surface treatment with air abrasion and erbium laser. Materials and Methods: One hundred twenty Al2O3 and 120 zirconia specimens measuring 3 × 3 × 0.7 mm3 were divided equally into three groups, and their surfaces treated as follows: either untreated (controls), air abraded with Al2O3 particles, or erbium-laser-treated at a power setting of 200 mJ. The surface of each specimen was then primed and bonded with one of two dual-cured resin cements (either SCP-100 Ceramic Primer and NAC-100 or Monobond S and Variolink II) using a 1-mm thick Tygon tube mold with a 0.75-mm internal bore diameter. After 24 hours and 6 months of water storage at 37◦C, a microshear bond strength test was performed at a crosshead speed of 1 mm/min. Surface morphology was examined using a confocal microscope, and failure modes were observed using an optical microscope. The data were analyzed using the Kaplan-Meier nonparametric survival analysis. Results: In the case of zirconia, air abrasion and Erbium:yttrium-aluminum-garnet (Er:YAG) laser treatment of the ceramic surface resulted in a significant reduction in the bond strengths of both resin cements after 6 months water storage; however, when the zirconia surface was left untreated, the SCP-100/NAC-100 group did not significantly reduce in bond strength. In the case of alumina, no treatment, air abrasion and Er:YAG laser treatment of the surface led to no significant reduction in the bond strengths of the three SCP-100/NAC-100 groups after 6 months water storage, whereas all three Monobond S/Variolink II groups showed a significant reduction. Conclusion: Er:YAG laser treatment of the zirconia surface did not result in a durable resin cement/ceramic bond; however, a durable bond between a conventional dual- cured resin cement and Procera All Ceram and Procera All Zirkon was formed using a ceramic primer containing the phosphate monomer, MDP, without any additional surface treatment. |
Palavras-chave: | Durability resin cement alumina zirconia adhesion air abrasion laser bond strength |
URI: | http://www.repositorio.ufba.br/ri/handle/ri/5493 |
Data do documento: | 2011 |
Aparece nas coleções: | Artigo Publicado em Periódico (Faculdade de Odontologia) |
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Durability of Resin Cement Bond to Aluminium Oxide and.pdf Restricted Access | 320,37 kB | Adobe PDF | Visualizar/Abrir Solicitar uma cópia |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.